스터드 볼트, 등급 8.8

간단한 설명:


  • 고강도 스터드, 너트, 와셔 및 연결 쌍은 철도, 교량, 산업 작업장, 슈퍼 백화점, 장소, 높은 시민 건물 및 풍력 타워 구조에 적용됩니다.
  • 제품 상세 정보

    제품 태그

     

    Contact us for 3rd party Fatigue Test certificates. [email protected]

    Fatigue tests: M56 M48 M42 M39 스터드 볼트

     

    Grade 8.8 stud Dimension: according to customer’s drawing.

    Grade 8.8 stud Thread: Metric, UNC

    Grade 8.8 stud Chemical composition: according to ISO898-1 requirements.

    Grade 8.8 stud Mechanical and physical properties: Table 3, ISO 898-1

    • Tensile strength, Rm: min 830MPa
    • Stress at 0.2% non-proportional elongation, Rp0.2: 660 MPa
    • Percentage elongation after fracture for machined test pieces, A: min 12% 
    • Percentage reduction of area after fracture for machined test pieces, Z: min 52%
    • Vickers hardness: 255-335 HV
    • Brinell hardness: 242-318 HBW
    • Rockwell hardness: 23-34HRC
    • Surface hardness: HV0.3 shall not be more than 30 Vickers points above the measured core hardness of the fastener when determination of both surface hardness and core hardness are carried out with HV 0,3.
    • Impact strength, Kv, 20 ℃, 0℃,-20℃,-40℃,-100℃: 27J Customerized
    • Surface integrity: ISO 6157-1

     

    The stud 볼트s that produced by Anyang Longteng have high performance, high tensile strength. Impact energy of 등급 8.8 볼트s at -40℃ can be 80J, which means quite good performance in low temperature. So that the studs can be used in cold weather oil platform. Highest tensile strength that Anyang Longteng Group can produce, is grade 12.9. The bolts provide steel structures and machineries high property to bend, strength, pre-stress, post-tension. So that the studs are widely applicated in wind turbine foundation, wind turbine blade,  shipbuilding, bridge, big machineries. roof supporting, etc. 

     

     